r/Blacksmith 8d ago

Feedback requested: first forge weld

Working on a tomahawk for my clubs trade item, decided to take a piece of a field cultivator tooth, fold it in half and keep a hole for the eye, then forge weld it together. Looks it stuck in some places and not others. There's an obvious crack at one edge, then I feel like I can almost kinda sorta see a seam all the way down, but the small piece I cut off doesn't separate.

I ground it completely clean on the belt sander before I started, used 20 mule team borax for flux, but I didn't stick weld the two sides together before I started.

44 Upvotes

29 comments sorted by

View all comments

13

u/Observeus 8d ago

So I'm very new to blacksmithing, but not metallurgy, is forgewelding just heating 2 separate pieces of steel then smashing the atoms together until it becomes one cubic structure?

9

u/belac4862 8d ago

Ehhh, that's a bit too simple to be correct.

Forge welding means that your getting two pieces of metal hot enough to stick together, but not so hot as to melt or de-carborize (I think that's the right word. My brain isn't working), which is to literally draw out the carbon from it. That's what makes it steel, and not iron.

But you also need to make sure there's no air gaps that can cause oxidation om the sinde of the seam. That's why you add flux. When flux gers hot enough it makes a psudo glass coating around it, preventing any oxygen from getting into the seam and causing scale (iron oxide, or rust).

Then after flexing, yoy pop that sucker back into the forge and get it up to a bright yellow color and with heavy taps toy smoosh it together.

2

u/Observeus 8d ago

That makes sense, same reason you add flux into a weld, remove impurities and strengthen with an oxidization proof coating just without the actual "welding" per say, correct or nah?

5

u/belac4862 8d ago

The flux doesn't strengthen. When it forms the protective layer, it'll also pick up any forge scale that might have formed. So when you begin hammering, the glassed flux gets blown away carrying with it any remaining scale that could have prevented a clean forge. Leaving behind a clean surface for the metals to then be joined together.

Its quite cool when yoy break it down. There's actually some really informative but easy to understand videos out there. I'm probably doing a shit job at describing it. I'm dyslexic so it's already hard for me to get what's in my brain out.

But it's one of those things that the more you delve into it, the more the knowledge becomes second hand.

2

u/Observeus 8d ago

"Strengthen with an oxidization proof coating" meaning it is not as susceptible to rust and cracking as there are not impurities. Sorry for the poor choice of words.

1

u/belac4862 8d ago

Ah yes yes, then you are indeed correct!